| Physical |
| Density | 0.96 | g/cm³ | ISO 1183 |
| MFR (2.16 kg, 190 °C) | 0.32 | g/10 min | ISO 1133-1 |
| Mechanical |
| Flexural Modulus (1% Secant) | 1350 | MPa | ISO 178 |
| Tensile Strength at Yield (23 °C, 50 mm/min) | 31 | MPa | ISO 527-2 |
| Tensile Elongation at Yield (23 °C, 50 mm/min) | 9.1 | % | ISO 527-2 |
| Tensile Strength at Break (23 °C, 50 mm/min) | ≥ 21 | MPa | ISO 527-2 |
| Tensile Elongation at Break (23 °C, 50 mm/min) | > 500 | % | ISO 527-2 |
| ESCR (Condition A, 50 °C, 10%, Igepal CO630, F50) | 40 | hr | ASTM D1693 |
| Shore Hardness (Shore D) | 64 | — | ISO 868 |
| Izod Impact Strength | | | |
| (Notched, -20 °C) | 42 | J/m | ASTM D256 |
| (Notched, 23 °C) | 343 | J/m | ASTM D256 |
| Thermal |
| Heat Deflection Temperature (0.46 MPa) | 57 | °C | ASTM D648 |
| OIT (190 °C) | > 20 | min | ASTM D3895 |
| Vicat Softening Temperature (10 N, 50 °C/h) | 128 | °C | ASTM D1525 |
| Melting Point | 134 | °C | ISO 11357-3 |